Carboxyl terminated polyester resins designed for use with triglycidyl isocyanurate
Resins for TGIC system
For matting Systems
- Good
- Very Good
- Excellent
Item code (Alymers) | Ratio (PE/TGIC) | Cure schedule 10min x object T(°C) | Acid Value | Viscosity (Poise, at 200°C) | approx. Tg (°C) | Flow | Resistance to | One-shot Matte | ||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Overbake | Gas oven | Impact | MEK rub | Blooming | ||||||||
General Industrial | ||||||||||||
TC3401 | 93/7 | 140 | 29-35 | 30-50 | 62 | |||||||
TC3502 | 93/7 | 150 | 28-34 | 30-40 | 62 | |||||||
TC3601 | 93/7 | 160 | 30-36 | 28-42 | 60 | |||||||
TC3606 | 93/7 | 160 | 30-36 | 33-47 | 63 | |||||||
TC3802 | 93/7 | 180 | 30-36 | 35-65 | 67 | |||||||
TC3016 | 93/7 | 200 | 28-36 | 40-60 | 65 | |||||||
TC4004 | 96/4 | 200 | 17-25 | 85-115 | 68 | |||||||
TC4008 | 96/4 | 200 | 18-24 | 85-115 | 62 | |||||||
TC8010 | 90/10 | 200 | 45-55 | 50-80 | 70 | |||||||
Architectural | ||||||||||||
TC3801 | 93/7 | 180 | 30-40 | 35-65 | 63 | |||||||
TC3824 | 93/7 | 180 | 32-38 | 65-85 | 70 | |||||||
TC3003 | 93/7 | 200 | 30-38 | 35-55 | 68 | |||||||
TC3004 | 93/7 | 200 | 30-36 | 35-55 | 67 | |||||||
TC3009 | 93/7 | 200 | 30-38 | 35-55 | 64 | |||||||
TC3011 | 93/7 | 200 | 28-36 | 35-55 | 62 | |||||||
TC3014 | 93/7 | 200 | 31-37 | 35-55 | 59 | |||||||
TC3021 | 93/7 | 200 | 30-38 | 35-55 | 67 | |||||||
TC3031 | 93/7 | 200 | 30-38 | 40-60 | 67 | |||||||
Super Durable | ||||||||||||
TC3605 | 93/7 | 160 | 30-36 | 28-42 | 63 | |||||||
TC3005 | 93/7 | 200 | 32-38 | 14-30 | 62 | |||||||
TC3006 | 93/7 | 200 | 29-35 | 35-65 | 64 | |||||||
TC3007 | 93/7 | 200 | 31-37 | 33-47 | 64 | |||||||
TC3015 | 93/7 | 200 | 32-38 | 15-25 | 62 | |||||||
TC8001 | 90/10 | 200 | 45-55 | 35-65 | 64 |